AN INVESTIGATION ON THE PRECIPITATION HARDENING OF TIG WELDED 2024 ALUMINUM ALLOY
Journal Name:
- Dokuz Eylül Üniversitesi Mühendislik Fakültesi Fen ve Mühendislik Dergisi
Key Words:
Keywords (Original Language):
Author Name | University of Author | Faculty of Author |
---|---|---|
Abstract (2. Language):
In this study, 2024 aluminum wrought alloy manufactured in the form of plates has been
welded with TIG welding method under protecting argon gas by using ER4043 electrode as
filler metal. The welding geometry is with 600
groove type. The specimens were solution heattreated under 492±3 0
C and quenched in water at room temperature. Then, they were aged
naturally and artificially. Artificial aging was performed at 125 0
C for 22 hours and at 190
0
C for 8,5 hours. Natural aging was performed at room temperature for one week. All
welding specimens were subjected to tension and Charpy tests. Microhardness and
microstructure of the welded specimens were determined.
Bookmark/Search this post with
Abstract (Original Language):
Bu çalışmada levha şeklinde üretilmiş olan 2024 alüminyum işlem alaşımı 600
’lik V
kaynak ağzı açılarak TIG kaynak yöntemi ile argon gazı altında ER4043 elektrot kullanılarak
birleştirilmiştir. Kaynaklanmış örnekler 492±3 0
C’de çözeltiye alınmış ve oda sıcaklığında su
verilmiştir, daha sonra bir kısmı doğal yaşlandırılırken bir kısmı da 125 0
C’de 22 saat ve 190
0
C’de 8.5 saat yapay yaşlandırılmıştır. Kaynaklı örnekler çekme ve çentik darbe deneylerine
tabi tutulmuştur. Kaynaklı bölgenin mikrosertliği ölçülüp içyapısı incelenmiştir.